Silica fume is a byproduct of producing silicon metal or
ferrosilicon alloys. One of the most beneficial uses for silica
fume is in concrete.
Because of its chemical and physical
properties, it is a very reactive pozzolan. Concrete
containing silica fume can have very high strength and can
be very durable. Silica fume is available from suppliers of
concrete admixtures and, when specified, is simply added
during concrete production. Placing, finishing, and curing
silica-fume concrete require special attention on the part of
the concrete contractor.
Silicon metal and alloys are
produced in electric furnaces as
shown in this photo. The raw
materials are quartz, coal, and
woodchips. The smoke that
results from furnace operation is
collected and sold as silica fume,
rather than being landfilled.
Perhaps the most important use
of this material is as a mineral
admixture in concrete.
Silica fume consists primarily of amorphous (non-crystalline) silicon dioxide (SiO2). The
individual particles are extremely small, approximately 1/100th the size of an average cement
particle. Because of its fine particles, large surface area, and the high SiO2 content, silica fume
is a very reactive pozzolan when used in concrete. The quality of silica fume is specified by
ASTM C 1240 and AASHTO M 307.
High-strength concrete is a very economical material for carrying vertical loads in high-rise
structures. Until a few years ago, 6,000 psi concrete was considered to be high strength. Today,
using silica fume, concrete with compressive strength in excess of 15,000 psi can be readily
produced. The structure shown at the above right used silica-fume concrete with a specified
compressive strength of 12,000 psi in columns reaching from the ground through the 57th story.
The greatest cause of concrete deterioration in the US today is corrosion induced by deicing or
marine salts. Silica-fume concrete with a low water content is highly resistant to penetration by chloride
ions. More and more transportation agencies are using silica fume in their concrete for construction of new
bridges or rehabilitation of existing structures.
Silica-fume concrete does not just happen. A specifier must make a conscious decision to include it in concrete to achieve desired concrete properties. Assistance in specifying silica-fume concrete for high strength or increased durability can be obtained from the SFA or from major admixture suppliers.
Silica fume for use in concrete is available in wet or dry forms. It is usually added during concrete production at a concrete plant as shown in the photo.Silica fume-concrete has been successfully produced in both central-mix and dry-batch plants. Assistance is readily available on all aspects of handling silica fume and using it to produce consistent, high-quality concrete.
Silica-fume concrete should be transported, placed,finished, and cured following the good concreting practices outlined by the American Concrete Institute. Flatwork containing silica fume concrete generally requires less finishing effort than conventional concrete. The photo shows the "one-pass" finishing process in which the silica-fume concrete is placed, consolidated, and textured
with little or no waiting time between operations. To gain the most benefits from using silica fume, the concrete must be cured effectively. The SFA or your concrete supplier can provide any necessary assistance concerning construction operations.